Z308 純鎳鑄鐵焊條
標準：
符合 GB EZNi-1
相當 AWS ENi-CI
說(shuō)明：
Z308是純鎳焊芯，強還原性石墨型藥皮的鑄鐵焊條，可交直流兩用。施焊時(shí)電弧穩定，操作方便，焊件可不預熱，其是鑄鐵冷焊焊條中，抗裂性、切削加工性、焊縫強度等綜合性能較好的一種焊條。
Z308 is a cast iron electrode with a pure nickel core and a strong reducing graphite coating. It can be used for both AC and DC. When welding, the arc is stable, the operation is convenient, and the weldment can be preheated. It is an electrode with better comprehensive performance such as crack resistance, machinability, and weld strength among cast iron cold welding electrodes.
用途：
可用于常溫或稍經(jīng)預熱（至200℃左右）的重要灰口鑄鐵，如：鑄鐵薄件的加工面，汽缸蓋、發(fā)動(dòng)機座、齒輪箱以及機床導軌、鑄鐵制成的機械零件等的焊、補。
It can be used for the welding of important gray cast irons at room temperature or slightly preheated (to about 200°C), such as: the machined surface of thin cast iron, cylinder heads, engine seats, gear boxes, machine tool guides, mechanical parts made of cast iron, etc. , Make up.
熔敷金屬化學(xué)成分（%）
| C | Si | Mn | Fe | Ni | S |
| ≤2.0 | ≤2.5 | ≤1.0 | ≤8.0 | ≥90 | ≤0.03 |
參考電流：AC或DC
| 焊條直徑（mm） | 2.5 | 3.2 | 4.0 | 5.0 |
| 焊接電流（A） | 50~80 | 80~100 | 110~140 | 150~180 |
注意事項：
1. 首先清除焊接部位的油污、砂、水、銹等污物，并視缺陷類(lèi)型，開(kāi)坡口、打止裂孔及熔池造型等準備措施。
2. 如填補大的空隙，應先從四周開(kāi)始堆焊一層，然后向中部逐步填滿(mǎn)。
3. 為避免母材熔化過(guò)多，減少白口層。施焊中，盡量采用小電流，短弧，窄道，短道，分散分段焊，每段焊道長(cháng)度一般不超過(guò)50mm，待溫度降至不燙手時(shí)再繼續施焊。并且施焊后立即錘擊焊縫以松馳應力防止裂紋。
4. 施焊前應將焊條在150℃左右烘焙一小時(shí)。
1. First, remove oil, sand, water, rust and other contaminants from the welding part, and prepare measures such as beveling, cracking prevention, and molten pool modeling depending on the type of defect.
2. To fill a large gap, start from the surrounding area by surfacing one layer, and then gradually fill it up to the middle.
3. In order to avoid excessive melting of the base material, reduce the white mouth layer. In welding, try to use small current, short arc, narrow track, short track, dispersed segment welding, the length of each segment of the weld generally does not exceed 50mm, and continue welding when the temperature drops to not hot. And immediately after welding, hammer the weld to relax the stress and prevent cracks.
4. The welding rod should be baked at about 150℃ for one hour before welding.
相關(guān)產(chǎn)品
白銅焊條Cu307
Z308 純鎳鑄鐵焊條
焊補鑄鐵用的鎳基鑄鐵焊條在鑄鐵焊接中屬于異質(zhì)焊縫的冷態(tài)焊焊條。藥皮為強還原性石墨型，交直流兩用，工藝性能良好，可全位置焊接。焊縫金屬不存在硬而脆的CFe3（滲碳體）即白口組織，所以焊縫金屬具有良好的加工性和承受塑性變形的能力。但熔合區由于母材成分熔化的影響，仍不可避免地會(huì )有不同程度的白口組織。為了減輕熔合區硬脆組織對焊后加工性能的不良影響，使其白口層盡量較少，較薄、且不連續，施焊時(shí)應該嚴格遵循冷焊工藝規定操作。另外，某些鑄件（如長(cháng)期在高溫、水蒸氣中工作的爐柵，鍋爐等），因其中的碳已被燒損，鑄件具有多空性，變得十分松脆而無(wú)法焊、補。
Z408 鎳鐵鑄鐵焊條
焊補鑄鐵用的鎳基鑄鐵焊條在鑄鐵焊接中屬于異質(zhì)焊縫的冷態(tài)焊焊條。藥皮為強還原性石墨型，交直流兩用，工藝性能良好，可全位置焊接。焊縫金屬不存在硬而脆的CFe3（滲碳體）即白口組織，所以焊縫金屬具有良好的加工性和承受塑性變形的能力。但熔合區由于母材成分熔化的影響，仍不可避免地會(huì )有不同程度的白口組織。為了減輕熔合區硬脆組織對焊后加工性能的不良影響，使其白口層盡量較少，較薄、且不連續，施焊時(shí)應該嚴格遵循冷焊工藝規定操作。另外，某些鑄件（如長(cháng)期在高溫、水蒸氣中工作的爐柵，鍋爐等），因其中的碳已被燒損，鑄件具有多空性，變得十分松脆而無(wú)法焊、補。
Z508 鎳銅鑄鐵焊條
焊補鑄鐵用的鎳基鑄鐵焊條在鑄鐵焊接中屬于異質(zhì)焊縫的冷態(tài)焊焊條。藥皮為強還原性石墨型，交直流兩用，工藝性能良好，可全位置焊接。焊縫金屬不存在硬而脆的CFe3（滲碳體）即白口組織，所以焊縫金屬具有良好的加工性和承受塑性變形的能力。但熔合區由于母材成分熔化的影響，仍不可避免地會(huì )有不同程度的白口組織。為了減輕熔合區硬脆組織對焊后加工性能的不良影響，使其白口層盡量較少，較薄、且不連續，施焊時(shí)應該嚴格遵循冷焊工藝規定操作。另外，某些鑄件（如長(cháng)期在高溫、水蒸氣中工作的爐柵，鍋爐等），因其中的碳已被燒損，鑄件具有多空性，變得十分松脆而無(wú)法焊、補。
Cu107 紫銅焊條
銅及銅合金焊條用途較廣，除了用紫銅焊條焊接紫銅外，目前采用較多的是用青銅焊條來(lái)焊接銅及銅合金、銅與鋼等。但銅及其合金的弧焊一般較鋼困難。這是由于銅及銅合金焊接時(shí)易產(chǎn)生金屬氧化、元素燒損、以及氣孔、裂縫和變形等。另外，銅及其合金的導熱性特別高致使焊條在引弧后往往不能使母材熔融，而產(chǎn)生熔滴飛散，故焊接銅及銅合金時(shí)該類(lèi)焊件焊前必須要有合理的預熱及用較大的焊接電流、直流反接，短弧垂直。焊后應對焊縫進(jìn)行適當錘擊，以消除應力及細化晶粒。另外，銅及其合金塑性好且不溶解碳，也不與碳化合生成脆硬組織，故銅及銅合金焊條也能用來(lái)焊補鑄鐵。